Dye Degradation Comparison Studies of Methylene Blue and Methyl Orange by Synthesized Zn Doped Fibrous Wollastonite.

Abhijit M * and Suresh Kumar B V

1 Dos in Earth Science, Manasagangothri, University of Mysore, Mysuru, Karnataka India

Corresponding author Email: abhijit.geology@gmail.com

DOI: http://dx.doi.org/10.12944/CWE.18.1.18

In this study, Zn-doped calcium silicate (Zn-WO) materials were successfully synthesized. As precursors, Ca (OH)2, SiO2, and ZnO were utilized, then the hydrothermal experiment was conducted for 6 hours at 1050°C. In this work, the behavior of two groups of raw materials exposed to isobaric and different temperature circumstances is described. The synthesized sample was examined using XRD, SEM, EDAX, Raman, BET, and UV-Vis spectroscopic techniques to understand the adsorbent's physicochemical characteristics, and the adsorbent's performance was evaluated. The energy band gap of 2.70 eV and 2.62 eV with the surface area calculated by BET of 92.4 m2/g and 112.6 m2/g for Zn-WO-1 and Zn-WO-2 respectively were found in this research. After 150 minutes of Zn-WO-1 and Zn-WO-2, the maximum amount of degradation by absorption under dark and sunlight photocatalytic activity compared with the two synthesized samples, 88.4% and 92.3% of methylene blue and 80.9% and 85.3% of methyl orange, took place.

Hydrothermal; Methylene blue; Methyl orange; Wollastonite

Copy the following to cite this article:

Abhijit M, Kumar B. V. S. Dye Degradation Comparison Studies of Methylene Blue and Methyl Orange by Synthesized Zn Doped Fibrous Wollastonite. Curr World Environ 2023;18(1). DOI:http://dx.doi.org/10.12944/CWE.18.1.18

Copy the following to cite this URL:

Abhijit M, Kumar B. V. S. Dye Degradation Comparison Studies of Methylene Blue and Methyl Orange by Synthesized Zn Doped Fibrous Wollastonite. Curr World Environ 2023;18(1).

Creative Commons License
This work is licensed under a Creative Commons Attribution 4.0 International License.